CUSTOMIZED
Substrate material: UVFS (Corning 7980 0F)
Dimensions: W=28.6 mm x H=14.3 mm +0/-0.1 mm
Thickness at high edge: 3.0 mm +/-0.1 mm
Coated area: min 27 mm x 14.3 mm
Clear aperture: min 24 mm x 12 mm elliptical
Surface quality, S1/S2: 20-10 S-D per CA
Surface flatness, S1/S2: <λ/6 @ 633 nm per CA (RWE and TWE <λ/10)
Wedge, face A | face B: 1 deg +/-10 arcmin
Protective chamfers: 0.2 - 0.4 mm x 45°
Chips: <0.2 mm stoned
Coatings (IBS):
S1 (Plane A, arrow marks): Ts<20% @ 725 nm - 875 nm, AOI=72 deg +/-2 deg, Tp>98% @ 725 nm - 875 nm, AOI=72 deg +/-2 deg
Tp/Ts extintion ratio: 5: 1 per surface
GDD Rs & Tp 0 fs^2 +/-50 fs^2
S2 (Plane B, wedge): SCC + ARp <0.7% @ 725 nm - 875 nm, AOI=72 deg +/-2 deg
LIDT:
>600 mJ/cm2, 500 ps, 10 Hz, 800 nm per CA (x2 as per ISO, 200 um)
>250 mJ/cm2, 100 ps, 10 Hz, 800 nm per CA (x2 as per ISO, 200 um)